Product Range:
CR123 - Black Economy Grade NR / SBR 70° shore
Suitable for a wide range of applications.
Due to the nature and economy of manufacture [an amount of RECLAIMED materials are blended with base polymer and fillers] minor surface deformations and blemishes may occur and materials may be more odorous than normal.
| Material Profile | See below |
| Thickness | 1mm to 50mm |
| Sheet Size | 1.4m wide in 5, 10 & 20m rolls |
| Finish | Smooth, Cloth, Smooth / Plate |
| Cutting | Standard press-tools |
Other grades, colours and finishes are available (subject to minimum batch quantities)
Search Results:
| Material | NR/SBR |
| Application | General Purpose |
| Store Hardness +/- 5º | 70 |
| Thickness | 1mm, 1.5mm, 2mm, 2.5mm, 3mm, 4mm, 5mm, 6mm, 8mm, 10mm, 12mm, 15mm, 19mm, 20mm, 25mm, 30mm, 40mm, 50mm |
| Temp. Range | -20°C to +70°C |
| Colour | Black |
| Insertion Req | No |
| Cloth/Plate | Cloth / Cloth, Cloth / Plate, Plate / Plate |
| Resistant To | N/A |
Technical Data:
| Stock Roll Sizes [mm x mm x m] |
Surface Finish | Weight [kg/M²] | Specifications Compound | Values [typical] |
| 1mm x 1400mm x 20m | SS | 1.50 | Colour | Black |
| 1.5mm x 1400mm x 20m | SS CC CS | 2.25 | Compound | NR / SBR |
| 2mm x 1400mm x 20m | SS CC CS | 3.00 | Density [specific gravity] | 1.5 |
| 2.5mm x 1400mm x 20m | SS CC CS | 3.75 | Hardness [degrees shore A] | 70° ± 5° |
| 3mm x 1400mm x 10m | SS CC CS | 4.50 | Tensile strength [Mpa] | 3 |
| 4mm x 1400mm x 10m | SS CC CS | 6.00 | Elongation at break | 150% |
| 5mm x 1400mm x 10m | SS CC | 7.50 | Minimum temperature | -20°C |
| 6mm x 1400mm x 10m | SS CC | 9.00 | Maximum temperature | +70°C |
| 8mm x 1400mm x 5m | SS | 12.00 | Compression set (70°C for 22 hours) % | 50 |
| 10mm x 1400mm x 5m | SS CS | 15.00 | ||
| 12mm x 1400mm x 5m | SS | 18.00 | ||
| 15mm x 1400mm x 5m | SS | 22.50 | ||
| 20mm x 1400mm x 5m | SS | 30.00 | ||
| 25mm x 1400mm x 5m | SS | 37.50 | ||
| 30mm x 1400mm x 5m | SS | 45.00 | ||
| 40mm x 1400mm x 5m | SS | 60.00 | ||
| 50mm x 2m x 1m | SS | 75.00 |