Product Range:
CR101 - Black ‘Economy’ Grade NR / SBR 45° shore
An 'economy' grade Natural Rubber and Styrene Butadiene rubber blend, It is used where a cheaper quality material will suit - in simple applications such as packing pieces, dust seals, protection pads etc where the materials is not coming under duress.
Due to the nature and economy of manufacture [an amount of RECLAIMED materials are blended with base polymer and fillers] minor surface deformations and blemishes may occur and materials may be more odorous than normal.
| Material Profile | See below |
| Thickness | 3mm to 10mm |
| Sheet Size | 1.4m wide in 5 & 10m rolls |
| Finish | Smooth both sides |
| Cutting | Standard press-tools |
Other grades, colours and finishes are available (subject to minimum batch quantities)
Search Results:
| Material | NR/SBR |
| Application | General Purpose |
| Store Hardness +/- 5º | 45 |
| Thickness | 3mm, 5mm, 6mm, 10mm |
| Temp. Range | -20°C to +70°C |
| Colour | Black |
| Insertion Req | No |
| Cloth/Plate | Plate / Plate |
| Resistant To | N/A |
Technical Data:
| Stock Roll Sizes [mm x mm x m] |
Surface Finish | Weight [kg/M²] | Specifications Compound | Values [typical] |
| 3mm x 1400mm x 10m | SS | 3.9 | Colour | Black |
| 5mm x 1400mm x 10m | SS | 6.5 | Compound | NR/SBR |
| 6mm x 1400mm x 10m | SS | 7.8 | Density [specific gravity] | 1.3 |
| 10mm x 1400mm x 5m | SS | 13 | Hardness [degrees shore A] | 45° ± 5° |
| Tensile strength [Mpa] | 6.0 | |||
| Elongation at break | 400 | |||
| Minimum temperature | -20°C | |||
| Maximum temperature | +70°C | |||
| Compression set (70°C for 22 hours) % | 50 |